29 August 2022 Variable composition in NiCrNx adhesion layers for protected silver mirrors and the effect on mirror durability
Kelsey A. Folgner, Samuel L. Dunscombe, Nicolas B. Liang, Chung-Tse Chu, Diana R. Alaan, Christopher J. Panetta, James D. Barrie
Author Affiliations +
Abstract
Various layer schemes are used to protect thin film silver mirrors from tarnish, corrosion, and degradation. One common design is based on the coating currently utilized by the twin Gemini astronomical telescopes, consisting of two very thin layers of nickel-chromium nitride (NiCrNx) on either side of the silver layer followed by a protective overcoat of silicon nitride (SiNx). Variations of this coating design have employed assorted NiCr- or Cr-based layers of varying thicknesses on either side of the silver, in efforts to achieve both high reflectivity and good durability. Generally, however, it is believed that reflectivity comes at the expense of durability. Ongoing work in our laboratory has explored the durability and corrosion behavior of various Gemini-style silver mirrors with NiCr- and Cr-based layers. Here, we present recent work on varying the Ni/Cr ratio in the NiCrNx adhesion layer above the silver and the effect on mirror durability, in terms of reflectance, scatter, and corrosion feature development during accelerated environmental exposure testing. By varying the adhesion layer Ni/Cr ratio from Ni-rich (90/10 Ni/Cr) to Cr-rich (0/100 Ni/Cr), it is possible to control the initial optical performance of the mirrors, as Ni-content is inversely related to reflectance. By varying the Ni/Cr ratio, it is also possible to control mirror durability, including the mechanism of corrosion feature development. This suggests that there may be an intermediate Ni/Cr composition with reduced Ni-content that improves reflectance without sacrificing durability.
Conference Presentation
© (2022) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Kelsey A. Folgner, Samuel L. Dunscombe, Nicolas B. Liang, Chung-Tse Chu, Diana R. Alaan, Christopher J. Panetta, and James D. Barrie "Variable composition in NiCrNx adhesion layers for protected silver mirrors and the effect on mirror durability", Proc. SPIE 12188, Advances in Optical and Mechanical Technologies for Telescopes and Instrumentation V, 121881Y (29 August 2022); https://doi.org/10.1117/12.2628337
Advertisement
Advertisement
RIGHTS & PERMISSIONS
Get copyright permission  Get copyright permission on Copyright Marketplace
KEYWORDS
Mirrors

Corrosion

Reflectivity

Silver

Coating

Chromium

Nickel

RELATED CONTENT


Back to Top