Laser densification of optical films

Brian D. Fabes; Brian J.J. Zelinski; Douglas J. Taylor; Lori Weisenbach; Sajiv Boggavarapu; David Z. Dent

doi:10.1117/12.132016

7 December 1992 Laser densification of optical films

Brian D. Fabes, Brian J.J. Zelinski, Douglas J. Taylor, Lori Weisenbach, Sajiv Boggavarapu, David Z. Dent

Author Affiliations +

Proceedings Volume 1758, Sol-Gel Optics II; (1992) https://doi.org/10.1117/12.132016
Event: San Diego '92, 1992, San Diego, CA, United States

Abstract

Sol-gel derived SiO₂-TiO₂ and WO₃ films were densified with a CO₂ laser. Laser fired SiO₂-TiO₂ films had higher optical loss (6 dB/cm) than similar films fired in a furnace (< 1 dB/cm). For coating shrinkages up to about 40% the increase in refractive index during firing was similar for both laser and furnace fired SiO₂-TiO₂ coatings. At higher shrinkages both anatase and rutile were observed in the laser fired coatings. Loss measurements of laser fired samples in this and, likely, in previous studies were made in crystalline coatings. It is proposed that this, at least in part, is the cause of the high optical losses typically measured in laser densified silica-titania waveguides. The electrochromic coloring behavior of the WO₃ films was examined using proton insertion. The coloring characteristics (< 20 s for 90% coloring) and bleaching characteristics (< 3 s for 90% bleaching) of laser fired WO₃ films were comparable to the coloring and bleaching characteristics of high-quality sol-gel derived films fired in a furnace. Optimal coloring was obtained using moderate laser energy densities (approximately 50 - 100 J/cm²). This optimum occurred with less shrinkage than for furnace fired electrochromic films with similar coloring behavior.

Citation Download Citation

Brian D. Fabes, Brian J.J. Zelinski, Douglas J. Taylor, Lori Weisenbach, Sajiv Boggavarapu, and David Z. Dent "Laser densification of optical films", Proc. SPIE 1758, Sol-Gel Optics II, (7 December 1992); https://doi.org/10.1117/12.132016

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

;

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE