In recent years, aluminum oxide films have found application in surface acoustic wave sensors. The paper presents the mechanical and physical properties of aluminum oxide (Al2O3) films obtained by the sol-gel method and subsequent sintering by high-temperature annealing. The synthesis of an aluminum oxide film from inorganic sols using the sol-gel technology was carried out. The effect of high-temperature treatment on the geometric dimensions, surface morphology, and hardness of Al2O3 films has been investigated. It was found that due to high-temperature sintering, the average values of film thickness and surface roughness are reduced by about 2 times. The effect of sintering temperatures on hardness suggests that with increasing temperature hardness of aluminum oxide film increases, and at sintering temperature of 800°C was 11.7±1.2 GPa.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.