Excellent optical properties of chalcogenide glasses make them interesting for optoelectronic devices in the visible (VIS) and, especially, in the near- and mid-infrared (NIR and MIR) spectral regions. The rare-earth (RE3+) doped Ga17Ge25As8.3S65 glasses were prepared in evacuated (~10−5 Pa) silica-glass ampoules which were heated up to 1000 °C at 2–4°C min-1, and then the melt was quenched. The absorption and photoluminescence spectra in the visible and near IR regions for GA1.7Ge25As8.3S65 doped with rare-earth RE+) ions (Sm3+, Nd3+, Pr3+, Dy3+ and co-doped with Ho3++Dy3+) are investigated. The energy transfer of the absorbed light in the broad band Urbach region of the host glass to the RE3+ ions is suggested for increasing the emission efficiency. The investigated Ga17Ge25As8.3S65 glasses doped with RE3+ ions are promising materials for optical amplifiers operating at 1300 and 1500 nm telecommunication windows.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.